Microscopy Morphology — Synthesis and structure of a non-van-der-Waals two-dimensional coordination polymer with superconductivity

2 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Isolated Cu3BHT single crystals · Single Crystal

Nion UltraSTEM 100 at 60 kV; exfoliated flakes imaged mainly in face-on orientation.

Context: pristine Cu3BHT single-crystal flakes
Measurement source: 2 · Single crystal structure characterization of Cu3BHT · Figure 1e; Supplementary Fig. 8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
In-plane kagome lattice observed	2D kagome lattice of Cu atoms	—	—	Qualitative Qualitative	2 · Single crystal structure characterization of Cu3BHT · Figure 1e; Supplementary Fig. 8

Cu3BHT micro-crystal array / multicrystalline film · Thin Film

FEI Quattro S, 5-30 kV; no supplementary metal coating required because of Cu3BHT conductivity.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu3BHT crystal cross-sectional area	exceeding 10^4 nm2	—	lower bound	Text Approximate	2 · Synthesis of Cu3BHT micro-crystal array · Figure 1d
Cu3BHT crystal length	lengths reaching several micrometers	—	—	Text Approximate	2 · Synthesis of Cu3BHT micro-crystal array · Figure 1d