Measurement evidence
Metal-organic framework nanomaterials as novel signal probes for electron transfer mediated ultrasensitive electrochemical immunoassay · Liu T.-Z., Hu R., Zhang X. et al. · Analytical Chemistry · 2016 · 12516-12523
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Au-MOFs-Ab2 signal nanoprobe · Powder
Ab2-modified MOFs imaged before and after negative voltage scanning.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| SEM morphology after negative voltage scanning | Ab2-modified MOFs imaged before and after negative voltage scanning; structure collapses/release mechanism inferred | — | — | Text Qualitative | 4 · Immunoassay Using MOF-Metal-Ion Probes |
Au-MOFs nanoparticles · Powder
TEM imaging of Au-MOFs and EDS confirmation of Au.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Au-MOF EDS Au atomic fraction | Au L atomic 7.12% | — | — | SI Table Exact Reported | 15 · Supporting Information · Figure S13 |
| Au-MOF EDS Au weight fraction | Au L weight 15.59% | — | — | SI Table Exact Reported | 15 · Supporting Information · Figure S13 |
| Au-MOF EDS Cu weight fraction | Cu K weight 28.64% | — | — | SI Table Exact Reported | 15 · Supporting Information · Figure S13 |
| Au-MOF EDS Mo weight fraction | Mo K weight 55.77% | — | — | SI Table Exact Reported | 15 · Supporting Information · Figure S13 |
| Au-MOF average diameter | average diameter of 100 nm | — | — | Text Rounded Reported | 5 · Characterization · Figure 2c,d |
as-prepared COF nanoparticles · Powder
TEM image of as-prepared COF nanoparticles.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| COF average nanoparticle size | average size of 200 nm | — | — | Text Rounded Reported | 4 · Characterization · Figure 1 |
Pt-COFs nanomaterial · Powder
TEM imaging of Pt-COFs plus EDS confirmation of Pt.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Pt nanoparticle loading morphology | large number of Pt NP black dots uniformly loaded; no agglomeration detected | — | — | Text Qualitative | 5 · Characterization · Figure 1c,d |
| Pt-COFs EDS Cu weight fraction | Cu K weight 82.83% | — | — | SI Table Exact Reported | 14 · Supporting Information · Figure S12 |
| Pt-COFs EDS Pt atomic fraction | Pt L atomic 6.32% | — | — | SI Table Exact Reported | 14 · Supporting Information · Figure S12 |
| Pt-COFs EDS Pt weight fraction | Pt L weight 17.17% | — | — | SI Table Exact Reported | 14 · Supporting Information · Figure S12 |