SQUID dc/ac magnetic susceptibility and hysteresis
Microcrystalline/crystalline powder of 1 · Powder
Samples in quartz tubes with eicosane; dc susceptibility 2-300 K at 0.1, 0.5 and 1 T; hysteresis sweep rate 2 mT/s.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Room-temperature chi_M T for 1 | 10.9 emu K/mol at 300 K | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Room-temperature chi_M T for 2 | 11.2 emu K/mol at 300 K | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Coercive field of 1 | 100 Oe | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Coercive field of 2 | 350 Oe | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Curie constant for 1 | C = 6.1 emu K/mol | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Curie constant for 2 | C = 5.90 emu K/mol | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Curie-Weiss theta for 1 | theta = 134 K | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Curie-Weiss theta for 2 | theta = 144 K | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure 8 |
| Magnetic ordering temperature of 1 | 8 K | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figures 8 and S10 |
| Magnetic ordering temperature of 2 | 12 K | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure S10 |
| Low-temperature saturation magnetization of 1 | 7.3 muB/mol | — | — | Text Rounded Reported | 6 · Magnetic Properties · Figure S11 |
| Low-temperature saturation magnetization of 2 | 7.11 muB/mol | — | — | Text Exact Reported | 7 · Magnetic Properties · Figure S12 |