Measurement evidence
Electrical conductivity and electroluminescence of a new anthracene-based metal-organic framework with π-conjugated zigzag chains · Chen D., Xing H., Su Z. et al. · Chemical Communications · 2016 · 2019-2022
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Single-crystal NNU-27 conductivity device · Single Crystal
Three cycles sweeping voltage from -5 V to 5 V for the same single crystal.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| repeat-sweep stability | I-V curves are almost identical when voltage was switched on-off several times | — | — | Text Qualitative | p003 · Electrical conductivity · Figure S5 |
Single-crystal NNU-27 conductivity device · Single Crystal
Single crystal immobilised between two conducting silver-resin contacts; measurements in dark under ambient/room-temperature air; voltage swept from -5 V to 5 V.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| average electrical conductivityMarked as a best value within this paper | 1.3 (+/-0.5) x 10^-3 S cm^-1 | 0.13 S m-1 | +/-0.5 x 10^-3 S cm^-1 | Text Rounded Reported | p003 · Electrical conductivity · Figure 2 |
| effective contact length | ca. 600 x 140 x 140 um; length interpreted as 600 um | — | — | Text Approximate | p003 · Electrical conductivity · Figure 2 |
| representative sample 3 current at +5 V | approximately +2.9 nA from Figure 2c | — | — | Figure Axis Approximate | p003 · Electrical conductivity · Figure 2c |
| I-V linearity | well-fitted linear dependence at ambient temperature | — | — | Text Qualitative | p003 · Electrical conductivity · Figure 2c |
| I-V sweep maximum voltage | 5 V | — | — | Text Exact Reported | p003 · Electrical conductivity · Figure 2 |
| I-V sweep minimum voltage | -5 V | — | — | Text Exact Reported | p003 · Electrical conductivity · Figure 2 |