Other — Tuning Electrical- and Photo-Conductivity by Cation Exchange within a Redox-Active Tetrathiafulvalene-Based Metal–Organic Framework

Measurement evidence

Other

Tuning Electrical- and Photo-Conductivity by Cation Exchange within a Redox-Active Tetrathiafulvalene-Based Metal–Organic Framework · Zhou Y., Yu F., Su J. et al. · Angewandte Chemie - International Edition · 2020 · 18763-18767

1 measurement group · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Thermogravimetric analysis on STA 449C thermal analysis system.

Thermogravimetric analysis

TTF@1 crystals · Single Crystal

N2 atmosphere; heating rate 10 deg C min-1 from 30 to 800 deg C.

Atmosphere: N2
Geometry: Powder/crystal bulk sample
Context: Thermal stability of exchanged TTF@1 and MV@1.
Measurement source: S13 · Figure S11 caption · Figure S11

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
decomposition temperature for TTF@1 and MV@1	350 deg C	623.15 K	—	Text Rounded Reported	S13 · Figure S11 discussion · Figure S11
MV@1 mass loss assigned to DMF removal	246 deg C, 12.70% loss	—	—	Figure Axis Rounded Reported	S13 · Figure S11 · Figure S11b
TTF@1 mass loss assigned to DMF removal	270 deg C, 23.30% loss	—	—	Figure Axis Rounded Reported	S13 · Figure S11 · Figure S11a