Porosity — Mixed proton-electron conductivity in a dynamic 3D metal-organic framework

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

H12-Al2-(DOBDP)3 (_d) · Powder

Water sorption at 298 K; Al sample degassed at 150 deg C and 1e-1 Pa vacuum for 12 h before isotherm.

Temperature: 298
Atmosphere: water vapour
Geometry: powder
Context: dehydrated pristine Al framework during adsorption
Measurement source: p006 · Water sorption and structure dynamics · Figure S20

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Al-MOF water BET surface areaMarked as a best value within this paper	586 m2/g	586 m^2/g	—	Text Rounded Reported	text after p027 · Surface area calculations · Figure S20
Al-MOF water uptake at P/P0 = 1Marked as a best value within this paper	365 cm3/g	365 cm^3/g	—	Text Rounded Reported	p006 · Water sorption and structure dynamics · Figure S20

H12-Fe2-(DOBDP)3 (_d) · Powder

Water sorption at 298 K; Fe sample degassed at 90 deg C and 1e-1 Pa vacuum for 2 h before isotherm.

Temperature: 298
Atmosphere: water vapour
Geometry: powder
Context: dehydrated pristine Fe framework during adsorption
Measurement source: p006 · Water sorption and structure dynamics · Figure S20

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Fe-MOF water BET surface area	403 m2/g	403 m^2/g	—	Text Rounded Reported	text after p027 · Surface area calculations · Figure S20
Fe-MOF water uptake at P/P0 = 1	295 cm3/g	295 cm^3/g	—	Text Rounded Reported	p006 · Water sorption and structure dynamics · Figure S20