Other — Lithium Ion Diffusion in a Metal-Organic Framework Mediated by an Ionic Liquid

3 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

ELT-bulk · Unknown

Hermetically sealed in aluminium pans under dried argon; heated to 473 K, cooled to 153 K, then reheated to 473 K at 5 K min^-1.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ELT-bulk glass transition peak temperature	endothermic peak at 192 K	—	—	Text Exact Reported	3 · Results and Discussion · Figure 4

ELT@Z100 · Pellet

Hermetically sealed in aluminium pans under dried argon; heated to 473 K, cooled to 153 K, then reheated to 473 K at 5 K min^-1.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ELT@Z100 broad endothermic heat-flow range	broad and weak endothermic heat flow from 200 to 240 K; onset around 200 K	—	—	Text Range	3 · Results and Discussion · Figure 4

ELT@Z75 · Pellet

Hermetically sealed in aluminium pans under dried argon; heated to 473 K, cooled to 153 K, then reheated to 473 K at 5 K min^-1.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ELT@Z75 absence of ELT-bulk glass transition anomaly	no heat anomaly appeared around 192 K	—	—	Text Qualitative	3 · Results and Discussion · Figure 4