Microscopy Morphology — Heteroatom-doped 3D porous carbon architectures for highly stable aqueous zinc metal batteries and non-aqueous lithium metal batteries

4 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Li@NOCA@CF · Electrode

Li deposition morphology in ether-based electrolyte at 1 mA cm-2 and 1 mAh cm-2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source

NOCA@CF · Electrode

Morphology and elemental distribution of MOF-derived NOCA@CF.

Context: Derived carbon target sample
Measurement source: 6 · 3.1. Synthesis and characterization of NOCA@CF · Fig. 1d-m

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
NOCA@CF active material areal loading	0.5-0.7 mg cm-2	—	range	Text Range	4 · 2.2. N/O dual-doped carbon array grown on Cu foam

ZIF-8@CF precursor · Electrode

Morphology of ZIF-8@CF precursor nanorod arrays.

Context: MOF-on-Cu-foam precursor
Measurement source: 3 · 3.1. Synthesis and characterization of NOCA@CF · Fig. 1a-c

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ZIF-8@CF nanorod diameter	1.2-1.5 um	—	range	Text Range	5 · 3.1. Synthesis and characterization of NOCA@CF · Fig. 1a-c
ZIF-8@CF nanorod length	10-12 um	—	range	Text Range	5 · 3.1. Synthesis and characterization of NOCA@CF · Fig. 1a-c

Zn@NOCA@CF · Electrode

Zn deposition behaviour on CF and NOCA@CF at 1 mA cm-2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source