cMOF Evidence Base
Electrical Transport — High-resolution structure of Zn3(HOTP)2 (HOTP = hexaoxidotriphenylene), a three-dimensional conductive MOF

Measurement evidence

Electrical Transport

High-resolution structure of Zn3(HOTP)2 (HOTP = hexaoxidotriphenylene), a three-dimensional conductive MOF · Zhang K.J., Chen T., Oppenheim J.J. et al. · Chemical Science · 2025 · 12416-12420

2 measurement groups · 7 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Four-probe electrical conductivity

Electrical conductivity

Zn3(HOTP)2 pellets pressed under 3, 6, and 9 tons for four-probe conductivity · Pellet

Pressed pellets measured as a function of applied pressing pressure at 3, 6, and 9 tons.

Geometry
pressed pellet, four-probe
Context
pristine Zn3(HOTP)2 pressed pellet
Measurement source
p003-p004 / journal pages 12418-12419 · Results and discussion · Table 1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Four-probe conductivity at 3 tons pressing pressure3.36 x 10^-5 S cm^-1——Table
Exact Reported		p004 / journal page 12419 · Results and discussion · Table 1
Four-probe conductivity at 6 tons pressing pressure7.78 x 10^-5 S cm^-1——Table
Exact Reported		p004 / journal page 12419 · Results and discussion · Table 1
Four-probe conductivity at 9 tons pressing pressureMarked as a best value within this paper1.04 x 10^-4 S cm^-1——Table
Exact Reported		p004 / journal page 12419 · Results and discussion · Table 1

Two-contact probe conductivity

Electrical conductivity

Polycrystalline pressed pellet of Zn3(HOTP)2 for two-contact probe conductivity · Pellet

Home-built two-probe in situ press set-up; linear I-V sweep from -1 to +1 V; Keithley 2450 source meter and Keithley 8608 test leads; ambient atmosphere.

Temperature
296
Atmosphere
ambient
Geometry
pressed pellet, two-contact probe
Context
pristine Zn3(HOTP)2 pressed pellet
Measurement source
p003 · Methods; Room temperature conductivity measurements · Figure S18
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Average two-contact probe conductivity2.05 x 10^-5 S cm^-1——Text
Exact Reported		p003 / journal page 12418 · Results and discussion · Figure S18
Highest two-contact probe conductivity5.4 x 10^-5 S cm^-1——Text
Exact Reported		p003 / journal page 12418 · Results and discussion · Figure S18
Prior reported conductivity higher comparison4.5 x 10^-2 S cm^-1——Text
Exact Reported		p003 / journal page 12418 · Results and discussion · Figure S18
Prior reported conductivity lower comparison8 x 10^-5 S cm^-1——Text
Exact Reported		p003 / journal page 12418 · Results and discussion · Figure S18