Other — Utilization of counter anions for charge transportation in the electrical device fabrication of Zn(ii) metal-organic frameworks

2 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

compound 1 crystals · Single Crystal

Nitrogen atmosphere, 100 mL min^-1 flow; used to check thermal stability before device fabrication.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BF4-associated weight loss	29.8% total at 220 C and 370 C	—	—	Text Exact Reported	17009 · TGA studies · Fig. 5a
higher-temperature decomposition weight loss	21.3% from Fig. 5a annotation	—	—	Visual Estimate Approximate	17010 · TGA studies · Fig. 5a
early weight loss	2.2% due to trapped moisture	—	—	Text Exact Reported	17009 · TGA studies · Fig. 5a

compound 2 crystals · Single Crystal

Nitrogen atmosphere, 100 mL min^-1 flow; used to check thermal stability before device fabrication.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
higher-temperature decomposition weight loss	26.1% from Fig. 5b annotation	—	—	Visual Estimate Approximate	17010 · TGA studies · Fig. 5b
SO3-associated sulfate loss	9.4% from Fig. 5b annotation; text says almost 9% from 220-300 C	—	—	Visual Estimate Approximate	17010 · TGA studies · Fig. 5b
initial water loss	14.6% from Fig. 5b annotation; text says initial almost 14%	—	—	Visual Estimate Approximate	17010 · TGA studies · Fig. 5b