Other — Two-Dimensional Conjugated Metal-Organic Frameworks with Large Pore Apertures and High Surface Areas for NO2 Selective Chemiresistive Sensing

Measurement evidence

Other

Two-Dimensional Conjugated Metal-Organic Frameworks with Large Pore Apertures and High Surface Areas for NO2 Selective Chemiresistive Sensing · Chen P., Su X., Wang C. et al. · Angewandte Chemie - International Edition · 2023 · e202306224

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Thermogravimetric analysis

HIOTP-Ni black powder · Powder

35-800 deg C under N2 with 10 deg C min-1 heating rate.

Atmosphere: N2
Context: pristine powders
Measurement source: S3 / S9 · General characterization; TGA · Figures S9-S10

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HIOTP-Cu temperature at 90% mass retained	198 deg C	—	—	Text Exact Reported	p002 · Thermal stability · Figure S10
HIOTP-Ni temperature at 90% mass retainedMarked as a best value within this paper	314 deg C	—	—	Text Exact Reported	p002 · Thermal stability · Figure S9