Measurement evidence
Missing-Linker 2D Conductive Metal Organic Frameworks for Rapid Gas Detection · Liu C., Gu Y., Liu C. et al. · ACS Sensors · 2021 · 429-438
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
aNi-HAB chemiresistive device · Electrode
Voltage sweep approximately -5 to +5 V, current read from SI Figure S4c.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| I-V air current at +5 V | approximately +5 nA at +5 V in air | — | — | Visual Estimate Approximate | 8 · Figure S4 · Figure S4c |
| I-V vacuum current at +5 V | near 0 nA at +5 V under vacuum | — | — | Visual Estimate Approximate | 8 · Figure S4 · Figure S4c |
aNi-HAB chemiresistive device · Electrode
aNi-HAB presaturated with RH; 1 V DC applied; current decay and plateau under various RH environments.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| aNi-HAB 100% RH saturated current | approximately 1.8e-8 A at 100% RH | — | — | Visual Estimate Approximate | 433 · Figure 5 · Figure 5a |
| aNi-HAB transient plateau current increase | plateau is 1-3 orders of magnitude larger than baseline | — | — | Text Range | 434 · Mechanism evaluations · Figure 5a |
cNi-HAB chemiresistive device · Electrode
cNi-HAB control under various RH environments; 1 V DC applied.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| cNi-HAB 100% RH saturated current | approximately 2.5e-8 A at 100% RH | — | — | Visual Estimate Approximate | 433 · Figure 5 · Figure 5b |
| cNi-HAB transient proton-conduction signature | similar proton conduction characteristic was not observed | — | — | Text Qualitative | 434 · Mechanism evaluations · Figure 5b |