Porosity — Missing-Linker 2D Conductive Metal Organic Frameworks for Rapid Gas Detection

Measurement evidence

Porosity

Missing-Linker 2D Conductive Metal Organic Frameworks for Rapid Gas Detection · Liu C., Gu Y., Liu C. et al. · ACS Sensors · 2021 · 429-438

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 adsorption-desorption BET, Micromeritics ASAP 2020

Gas sorption and porosity

as-synthesized missing-linker aNi-HAB solid · Powder

Sample heated to 100 deg C under dynamic vacuum of 4 mtorr until outgas rate <2 mtorr/min.

Atmosphere: N2 adsorption; vacuum outgas
Geometry: powder
Context: pristine target
Measurement source: 4 · General Characterizations · Figure S4b

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	159.906 m2/g	—	—	Text Exact Reported	431 · Synthesis of conductive 2D MOF · Figure S4b
Average pore size	2.23 nm	—	—	Text Exact Reported	431 · Synthesis of conductive 2D MOF · Figure S4b