Diffraction Structure — Efficient MOF-Sensitized Solar Cells Featuring Solvothermally Grown [100]-Oriented Pillared Porphyrin Framework-11 Films on ZnO/FTO Surfaces

3 measurement groups · 10 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

bulk PPF-11 crystals · Single Crystal

Cu Kalpha radiation, Rigaku Ultima IV; as-synthesised crystals

Context: pristine PPF-11 bulk
Measurement source: 3198 · Bulk PPF-11 synthesis and characterization · Figure 1b

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
bulk preferred orientation	[001] direction	—	—	Qualitative Qualitative	3198 · Bulk PPF-11 synthesis and characterization · Figure 1b
bulk PPF-11 PXRD low-angle peak	2theta = 12.6	—	—	Text Rounded Reported	3198 · Bulk PPF-11 synthesis and characterization · Figure 1b
bulk PPF-11 PXRD low-angle peak	2theta = 18.9	—	—	Text Rounded Reported	3198 · Bulk PPF-11 synthesis and characterization · Figure 1b
bulk PPF-11 PXRD low-angle peak	2theta = 6.3	—	—	Text Rounded Reported	3198 · Bulk PPF-11 synthesis and characterization · Figure 1b

C60-doped PPF-11 crystals · Powder

C60-doped PPF-11 compared with undoped/bulk and films

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
PXRD after C60 infiltration	mostly unchanged; structure and crystallinity largely intact	—	—	Text Qualitative	3201 · Doping PPF-11 with C60 · Figure S6

[100]-oriented PPF-11 film on TCPP-coated ZnO-FTO · Electrode

Solvothermally grown PPF-11/ZnO film on ZnO-FTO

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
film preferred orientation	[100] oriented PPF-11 film	—	—	Qualitative Qualitative	3199 · Spontaneous solvothermal growth · Figure 1b
film PXRD [100] peak	2theta about 15	—	—	Text Approximate	3199 · Spontaneous solvothermal growth · Figure 1b
film PXRD [100] peak	2theta about 22.5	—	—	Text Approximate	3199 · Spontaneous solvothermal growth · Figure 1b
film PXRD [100] peak	2theta about 30	—	—	Text Approximate	3199 · Spontaneous solvothermal growth · Figure 1b
film PXRD [100] peak	2theta about 7.5	—	—	Text Approximate	3199 · Spontaneous solvothermal growth · Figure 1b