Diffraction Structure — A novel Sn-based coordination polymer with high-efficiency and ultrafast lithium storage

Measurement evidence

Diffraction Structure

A novel Sn-based coordination polymer with high-efficiency and ultrafast lithium storage · Zhang X., Han L., Li J. et al. · Journal of Materials Science and Technology · 2022 · 156-164

1 measurement group · 11 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Powder X-ray diffraction with Cu Kalpha radiation and Le Bail profile fitting

X-ray diffraction and scattering

as-prepared Sn-DHTPA powder · Powder

Scan rate 10 deg min^-1; Winplotr Le Bail refinement

Context: pristine Sn-DHTPA powder
Measurement source: p002 / article p.157 · Experimental - Material characterizations · Figure 1a; Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
unit-cell a parameter	a = 7.9268 A	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
unit-cell alpha angle	alpha = 90 deg	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
unit-cell b parameter	b = 7.926 A	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
unit-cell beta angle	beta = 90 deg	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
unit-cell c parameter	c = 9.1025 A	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
unit-cell gamma angle	gamma = 90 deg	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
unit-cell volume	571.95 A^3	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
crystal system	Tetragonal	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
crystallographic density	4.90 g/cm3	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
empirical formula	H4O8Sn6	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1
space group	P-421c	—	—	Table Exact Reported	p003 / article p.158 · Results and Discussion · Table 1