background cyclic voltammetry on bare FTO
bare FTO control electrode · Electrode
bare FTO with 36 mM [Co(bpy)3]3+ at 50 mV s-1 in DMF; 0.5 M LiClO4 supporting electrolyte
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|
Electrochemistry Application — Beyond diffusion: ion and electron migration contribute to charge transport in redox-conducting metal-organic frameworks
Measurement evidence
Electrochemistry Application
Beyond diffusion: ion and electron migration contribute to charge transport in redox-conducting metal-organic frameworks · Johnson B.A., Castner A.T., Agarwala H. et al. · Chemical Science · 2025 · 5214-5222
3 measurement groups · 3 results
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
cyclic voltammetry of [Co(bpy)3]3+ on glassy carbon
[Co(bpy)3]3+ on glassy carbon · Electrode
3 mM [Co(bpy)3]3+ in 0.5 M LiClO4/DMF; 0.071 cm2 glassy carbon disk; 100 mV s-1
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co(III)/Co(II) formal potential on glassy carbonMarked as a best value within this paper | E0_A/B = 0.27 V vs SCE | — | — | Caption Rounded Reported | p028 / SI page S28 · Figures · Figure S9 |
cyclic voltammetry without [Co(bpy)3]3+
Zn(NDI)@FTO thin film · Thin Film
Zn(NDI)@FTO in 0.5 M LiClO4/DMF; scan rates 1 to 500 mV s-1
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electroactive surface concentration of NDI linkers from slow CV | 1 x 10^-7 mol cm^-2 | — | — | Text Rounded Reported | p004 / journal page 5217 · Results and discussion · Fig. S7a |
| total redox-active linker concentrationMarked as a best value within this paper | C0P = 1 M | — | approximately | Text Approximate | p004 / journal page 5217 · Results and discussion |