Measurement evidence
Highly Porous, Electrically Conductive Two-Dimensional Nickel–Hexaaminodehydrobenzoannulene Frameworks · Ohkubo E., Suzuki M., Aizawa N. et al. · Journal of the American Chemical Society · 2025 · 31940-31951
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Ni3(HI12)2 activated powder · Powder
N2 flow 200 mL/min, 40-600 C, 5 C min-1; activated under N2 at 100 C for 1 h immediately before measurement
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| decomposition onset | around 155 C | — | — | Text Approximate | S18 · S2-6 · Figure S7b |
Ni3(HI18)2 activated powder · Powder
N2 flow 200 mL/min, 40-600 C, 5 C min-1; activated under N2 at 100 C for 1 h immediately before measurement
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| decomposition onset | approximately 180 C | — | — | Text Approximate | S18 · S2-6 · Figure S7c |
Ni3(HITP)2 activated powder · Powder
N2 flow 200 mL/min, 40-600 C, 5 C min-1; activated under N2 at 100 C for 1 h immediately before measurement
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| decomposition onset | around 180 C | — | — | Text Approximate | S18 · S2-6 · Figure S7a |