Other — Upgrading Structural Conjugation in Three-Dimensional Ni-Based Metal-Organic Frameworks for Promoting Electrical Conductivity and Specific Capacitance

2 measurement groups · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

as-synthesised Ni-BPE crystals · Single Crystal

Netzsch STA409pc; 20 C/min from 30 to 800 C under nitrogen

Atmosphere: nitrogen
Geometry: powder
Context: pristine target MOF
Measurement source: p. 18084 · Experimental Section - Materials and Methods · Figure 2c

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Ni-BPE no-weight-loss stability thresholdMarked as a best value within this paper	without weight loss until 400 C	—	—	Text Rounded Reported	p. 18087 · XPS, PXRD, IR, and TGA Characterization · Figure 2c

as-synthesised Ni-BPY crystals · Single Crystal

Netzsch STA409pc; 20 C/min from 30 to 800 C under nitrogen

Atmosphere: nitrogen
Geometry: powder
Context: pristine control MOF
Measurement source: p. 18087 · XPS, PXRD, IR, and TGA Characterization · Figure 2c

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Ni-BPY TGA weight loss at 230 C	about 35% at only 230 C	—	—	Text Approximate	p. 18087 · XPS, PXRD, IR, and TGA Characterization · Figure 2c