Measurement evidence
Multifunctional coordination polymers based on copper with modified nucleobases, easily modulated in size and conductivity · Vegas V.G., Maldonado N., Castillo O. et al. · Journal of Inorganic Biochemistry · 2019 · 110805
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
CP1 turquoise needle-shaped single crystals · Single Crystal
Graphite paste contacts and 25 um wolframium wires; voltage swept from +10 to -10 V.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| CP1 electrical conductivity at 300 K | 5.0 x 10^-9 S cm^-1 | — | — | Text Rounded Reported | 4 · 3.2.1. Electrical properties |
CP1 exposed to iodine vapour · Single Crystal
CP1 exposed to iodine vapour at ambient temperature and pressure for different times; same electrical method and voltage range as pristine crystals.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| CP1 iodine-doping conductivity enhancement | increase by two orders of magnitude | — | — | Calculated From Reported Approximate | 5 · 3.2.1. Electrical properties · Table 1 |
| CP1 conductivity after 0 min iodine exposure | 0 min: 5.0 x 10^-9 S/cm | — | — | Table Exact Reported | 7 · 3.2.1. Electrical properties · Table 1 |
| CP1 conductivity after 15 min iodine exposure | 15 min: 2.1 x 10^-8 S/cm | — | — | Table Exact Reported | 7 · 3.2.1. Electrical properties · Table 1 |
| CP1 conductivity after 30 min iodine exposure | 30 min: 3.3 x 10^-8 S/cm | — | — | Table Exact Reported | 7 · 3.2.1. Electrical properties · Table 1 |
| CP1 conductivity after 60 min iodine exposure | 60 min: 8.0 x 10^-8 S/cm | — | — | Table Exact Reported | 7 · 3.2.1. Electrical properties · Table 1 |
| CP1 conductivity after 720 min iodine exposure | 720 min: 9.9 x 10^-8 S/cm | — | — | Table Exact Reported | 7 · 3.2.1. Electrical properties · Table 1 |
| CP1 conductivity after 810 min iodine exposure | 810 min: 1.0 x 10^-7 S/cm | — | — | Table Exact Reported | 7 · 3.2.1. Electrical properties · Table 1 |
CP1 turquoise needle-shaped single crystals · Single Crystal
Conductivity versus temperature from 300 K to 380 K; activation energy from ln(conductivity) versus 1/T.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| CP1 electrical activation energy | 0.84 eV | — | — | Text Rounded Reported | 5 · 3.2.1. Electrical properties · Fig. S9 |
| CP1 conductivity at 300 K in temperature-dependent run | 5.1 x 10^-9 S cm^-1 at 300 K | — | — | Text Rounded Reported | 5 · 3.2.1. Electrical properties · Fig. S8 |
| CP1 conductivity at 373 K | 9.4 x 10^-7 S cm^-1 at 373 K | — | — | Text Rounded Reported | 5 · 3.2.1. Electrical properties · Fig. S8 |
CP2 light-blue single crystals · Single Crystal
Graphite paste contacts and 25 um wolframium wires; voltage swept from +10 to -10 V.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| CP2 electrical conductivity at 300 K | 3.40 x 10^-11 S cm^-1 | — | — | Text Rounded Reported | 4 · 3.2.1. Electrical properties |
CP3 yellow single crystals · Single Crystal
Graphite paste contacts and 25 um wolframium wires; voltage swept from +10 to -10 V.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| CP3 electrical conductivity at 300 KMarked as a best value within this paper | 1.8 x 10^-7 S cm^-1 | — | — | Text Rounded Reported | 4 · 3.2.1. Electrical properties |