Microscopy Morphology — Multifunctional coordination polymers based on copper with modified nucleobases, easily modulated in size and conductivity

4 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

microCP1 after ultrasound sonication · Nanosheet

CP1 suspension sampled after 1 h sonication and before centrifugation; aliquot deposited on SiO2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CP1 size after 1 h sonication	until one micron long	—	approximate	Figure Axis Approximate	7 · 3.2.2. Nanoprocessing · Fig. 6b

nanoCP1 supernatant flakes · Nanosheet

Supernatant after 1 h sonication and 3000 rpm centrifugation for 2 min; aliquot deposited on SiO2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
nanoCP1 flake width after centrifugation	approximately 200 nm width	—	approximately	Figure Axis Approximate	7 · 3.2.2. Nanoprocessing · Fig. 6c
Fraction of initial CP1 nanoprocessed	55% of the initial material	—	—	Text Rounded Reported	7 · 3.2.2. Nanoprocessing · Fig. 6

CP1 turquoise needle-shaped single crystals · Single Crystal

Original millimetre CP1 crystals imaged before ultrasound treatment.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Original CP1 crystal length before sonication	2-2.6 mm	—	range	Caption Range	7 · 3.2.2. Nanoprocessing · Fig. 6a

nanoCP1 supernatant flakes · Nanosheet

Aliquots of CP1 suspension deposited on SiO2 after sonication and centrifugation.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source