Other — Conductive Lanthanide Metal-Organic Frameworks with Exceptionally High Stability

3 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

as-synthesised Gd4-MOF single crystals · Single Crystal

under atmosphere

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CF3SO3- loss temperature	about 350 C	—	—	Caption Approximate	7 · Figure S7 caption · Figure S7
remaining mass after CF3SO3- loss	about 83.3 %	—	—	Caption Approximate	7 · Figure S7 caption · Figure S7
thermal stability limit by TGA	stable up to about 300 C	—	—	Caption Approximate	7 · Figure S7 caption · Figure S7
mass loss assigned to free water	7.0 % between 50 and 100 C	—	—	Caption Exact Reported	7 · Figure S7 caption · Figure S7

as-synthesised Lu4-MOF single crystals · Single Crystal

under atmosphere

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CF3SO3- loss temperature	about 350 C	—	—	Caption Approximate	13 · Figure S23 caption · Figure S23
remaining mass after CF3SO3- loss	about 84.1 %	—	—	Caption Approximate	13 · Figure S23 caption · Figure S23
thermal stability limit by TGA	stable up to about 300 C	—	—	Caption Approximate	13 · Figure S23 caption · Figure S23
mass loss assigned to free water	6.7 % between 50 and 100 C	—	—	Caption Exact Reported	13 · Figure S23 caption · Figure S23

as-synthesised Tm4-MOF single crystals · Single Crystal

under atmosphere

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CF3SO3- loss temperature	about 350 C	—	—	Caption Approximate	13 · Figure S22 caption · Figure S22
remaining mass after CF3SO3- loss	about 83.8 %	—	—	Caption Approximate	13 · Figure S22 caption · Figure S22
thermal stability limit by TGA	stable up to about 300 C	—	—	Caption Approximate	13 · Figure S22 caption · Figure S22
mass loss assigned to free water	6.8 % between 50 and 100 C	—	—	Caption Exact Reported	13 · Figure S22 caption · Figure S22