Microscopy Morphology — Radiation-Induced in Situ Construction of 2D Conductive Defect-Rich Metal-Organic Frameworks for High-Performance Supercapacitor

2 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cu-CAT-Rad · Powder

Morphology, 100-facet lattice fringes, diffraction and elemental ratios

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
EDS C atomic proportion	72.34 at%	—	+/- 0.07	SI Table Rounded Reported	10 · Section S4 · Table S2
EDS Cu/C atomic ratio	8.47	—	+/- 0.61	SI Table Rounded Reported	10 · Section S4 · Table S2
EDS Cu atomic proportion	6.13 at%	—	+/- 0.44	SI Table Rounded Reported	10 · Section S4 · Table S2
EDS N atomic proportion	2.00 +/- 0.34 at%	—	+/- 0.34	SI Table Rounded Reported	10 · Section S4 · Table S2
EDS O atomic proportion	19.53 +/- 0.71 at%	—	+/- 0.71	SI Table Rounded Reported	10 · Section S4 · Table S2
HR-TEM 100-facet lattice fringe	d100 = 1.84 nm	—	—	Text Rounded Reported	2 · Results and Discussion · Figure 2e

Cu-CAT-Sol · Powder

Morphology, 100-facet lattice fringes, diffraction and elemental ratios

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
EDS C atomic proportion	76.24 at%	—	+/- 0.71	SI Table Rounded Reported	10 · Section S4 · Table S1
EDS Cu/C atomic ratio	7.72	—	+/- 1.69	SI Table Rounded Reported	10 · Section S4 · Table S1
EDS Cu atomic proportion	5.89 at%	—	+/- 1.34	SI Table Rounded Reported	10 · Section S4 · Table S1
EDS N atomic proportion	0.65 +/- 0.52 at%	—	+/- 0.52	SI Table Rounded Reported	10 · Section S4 · Table S1
EDS O atomic proportion	17.23 +/- 1.53 at%	—	+/- 1.53	SI Table Rounded Reported	10 · Section S4 · Table S1
HR-TEM 100-facet lattice fringe	d100 = 1.77 nm	—	—	Text Rounded Reported	2 · Results and Discussion · Figure 2b