Porosity — Benign preparation of metal–organic frameworks of trimesic acid and Cu, Co or Ni for potential sensor applications

3 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

TMA-Co(II) powder · Powder

TriStar II Micromeritics; samples kept at 50 deg C for 3 days and degassed at 80 deg C for 8 h before liquid-N2 adsorption-desorption.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	0.11 m2/g	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Pore size	not measured / dash in table	—	—	Table Qualitative	p005 · MOF Characterization · Table II
Pore volume	not measured / dash in table	—	—	Table Qualitative	p005 · MOF Characterization · Table II
Gravimetric yield	45.6 +/- 10.1%	—	10.1%	Table Exact Reported	p005 · MOF Characterization · Table II

TMA-Cu(II) powder · Powder

TriStar II Micromeritics; samples kept at 50 deg C for 3 days and degassed at 80 deg C for 8 h before liquid-N2 adsorption-desorption.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface areaMarked as a best value within this paper	330.64 m2/g	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Pore sizeMarked as a best value within this paper	155.62 Angstrom	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Pore volumeMarked as a best value within this paper	0.0676 cm3/g	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Gravimetric yieldMarked as a best value within this paper	67.5 +/- 5.2%	—	5.2%	Table Exact Reported	p005 · MOF Characterization · Table II

TMA-Ni(II) powder · Powder

TriStar II Micromeritics; samples kept at 50 deg C for 3 days and degassed at 80 deg C for 8 h before liquid-N2 adsorption-desorption.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	0.91 m2/g	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Pore size	140.43 Angstrom	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Pore volume	0.0044 cm3/g	—	—	Table Exact Reported	p005 · MOF Characterization · Table II
Gravimetric yield	45.9 +/- 9.6%	—	9.6%	Table Exact Reported	p005 · MOF Characterization · Table II