Measurement evidence
Thousand-fold increase in O2electroreduction rates with conductive MOFs · Mariano R.G., Wahab O.J., Rabinowitz J.A. et al. · ACS Central Science · 2022 · 975-982
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
0.8 mg cm^-2 Ni3(HITP)2 + 10 wt% PTFE GDE · Electrode
SEM cross-section and plan-view imaging of 0.8 mg cm^-2 Ni3(HITP)2 + 10% PTFE GDE.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| PTFE domain size in modified GDE | ~300-500 nm domains between ~200-400 nm Ni3(HITP)2 clusters | — | — | Text Range | SI p.S12 · Supplementary text 3 · Figure S33 |
As-synthesised Ni3(HITP)2 powder · Powder
Powder samples dispersed on carbon tape; Zeiss Merlin HR-SEM with InLens detector, 2-4 kV.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co3(HITP)2 and Cu3(HITP)2 particle-cluster size | ~100-200 nm nanoparticulate clusters | — | — | Text Range | SI p.S9 · Supplementary text 1 · Figure S15 |
| Ni3(HITP)2 crystallite size | 50-200 nm crystallites agglomerated into 1 um wide clusters | — | — | Text Range | main article p.976 · Results and Discussion · Figure S4 |