Porosity — Thousand-fold increase in O2electroreduction rates with conductive MOFs

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

As-synthesised Co3(HITP)2 powder · Powder

N2 adsorption at 77 K for Co3(HITP)2 and Cu3(HITP)2 powders.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Co3(HITP)2 BET surface area	415.34 +/- 0.59 m2 g^-1	—	+/- 0.59 m2 g^-1	Figure Axis Exact Reported	SI p.S26 · Supplementary figures · Figure S14A
Cu3(HITP)2 BET surface area	245.45 +/- 0.84 m2 g^-1	—	+/- 0.84 m2 g^-1	Figure Axis Exact Reported	SI p.S26 · Supplementary figures · Figure S14B

As-synthesised Ni3(HITP)2 powder · Powder

N2 adsorption at 77 K after activation at 373 K under dynamic vacuum / 100 C overnight.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Ni3(HITP)2 BET surface area from Figure S3 inset	802.02 +/- 0.52 m2 g^-1	—	+/- 0.52 m2 g^-1	Figure Axis Exact Reported	SI p.S15 · Supplementary figures · Figure S3
Ni3(HITP)2 BET surface areaMarked as a best value within this paper	802 +/- 0.8 m2 g^-1	—	+/- 0.8 m2 g^-1	Text Exact Reported	main article p.976 · Results and Discussion · Figure S3