Electrical Transport — Redox-active conductive metal-organic framework with high lithium capacities at low temperatures

Measurement evidence

Electrical Transport

Redox-active conductive metal-organic framework with high lithium capacities at low temperatures · Kumar Y., Kim T.H., Subiyanto I. et al. · Journal of Materials Chemistry A · 2024 · 21732-21743

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

four-probe conductivity

Electrical conductivity

SKIER-5 cyan solid powder · Powder

Measured at room temperature by CMT-SR2000N under appropriate pressure without paste

Temperature: room temperature
Geometry: four-probe device; powder under pressure, exact geometry not reported
Context: pristine framework powder
Measurement source: 21734 · Synthesis and materials characterization

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
room-temperature electrical conductivityMarked as a best value within this paper	8 mS m^-1 at room temperature	0.008 S m^-1	—	Text Exact Reported	21734 · Synthesis and materials characterization
SI comparison-table electrical conductivity	10^-8 S cm^-1	0.000001 S m^-1	—	SI Table Rounded Reported	S8 · Table S2 · Table S2