Porosity — Redox-active conductive metal-organic framework with high lithium capacities at low temperatures

Measurement evidence

Porosity

Redox-active conductive metal-organic framework with high lithium capacities at low temperatures · Kumar Y., Kim T.H., Subiyanto I. et al. · Journal of Materials Chemistry A · 2024 · 21732-21743

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 sorption isotherm

Gas sorption and porosity

SKIER-5 cyan solid powder · Powder

N2 adsorption/desorption at 77 K; BET surface area reported

Temperature: 77
Atmosphere: N2
Context: pristine framework powder
Measurement source: 21734 · Synthesis and materials characterization · Figure S11

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface areaMarked as a best value within this paper	23.195 m2 g^-1	—	—	Text Exact Reported	21734 · Synthesis and materials characterization · Figure S11