Porosity — High-Performance H2S Sensors to Detect SF6 Leakage

3 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Co1.8Ni1.2(HITP)2 powder · Powder

N2 adsorption at 77 K after thermal treatment under dynamic vacuum at 90 C.

Temperature: 77
Atmosphere: N2
Context: pristine target mixed-metal powder
Measurement source: 3 · 2.1. Sample Preparation and Characterization · Figure S11

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	260 m2 g-1	—	—	SI Table Exact Reported	17 · Figure S11 · Figure S11
BJH pore-size distribution peak	0.51 nm	—	—	Caption Rounded Reported	17 · Figure S11 · Figure S11

Co3(HITP)2 powder · Powder

N2 adsorption at 77 K after thermal treatment under dynamic vacuum at 90 C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	362 m2 g-1	—	—	SI Table Exact Reported	17 · Figure S11 · Figure S11
BJH pore-size distribution peak	0.48 nm	—	—	Caption Rounded Reported	17 · Figure S11 · Figure S11

Ni3(HITP)2 powder · Powder

N2 adsorption at 77 K after thermal treatment under dynamic vacuum at 90 C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface areaMarked as a best value within this paper	460 m2 g-1	—	—	SI Table Exact Reported	17 · Figure S11 · Figure S11
BJH pore-size distribution peak	0.49 nm	—	—	Caption Rounded Reported	17 · Figure S11 · Figure S11