Measurement evidence
Superior Charge Transport in Ni-Diamine Conductive MOFs · Wang J., Chen T., Jeon M. et al. · Journal of the American Chemical Society · 2024 · 20500-20507
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Pristine Cu3(HITT)2 black powder · Powder
Heating rate 2.0 deg C/min under N2 gas flow of 5 mL/min on platinum pan, room temperature to 800 deg C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| guest solvent removal temperature | likely eliminated before reaching ~80 °C | — | — | Text Approximate | 20502 · Results and discussion · Figure S18 |
| major framework weight loss onset | starting at 200 °C | — | — | Text Approximate | 20502 · Results and discussion · Figure S18 |
Pristine Ni3(HITT)2 black powder · Powder
Heating rate 2.0 deg C/min under N2 gas flow of 5 mL/min on platinum pan, room temperature to 800 deg C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| guest solvent removal temperature | likely eliminated before reaching ~80 °C | — | — | Text Approximate | 20502 · Results and discussion · Figure S18 |
| major framework weight loss onset | above 300 °C | — | — | Text Approximate | 20502 · Results and discussion · Figure S18 |