Electrical Transport — From 0D to 2D: Microwave-assisted synthesis of electrically conductive metal-organic frameworks with controlled morphologies

3 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

0D spherical Cu-HHTP powder · Powder

Pressed pellet prepared with approximately 5 mg material in a 5 mm diameter die under 1.5 tons pressure.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
0D Cu-HHTP powder electrical conductivityMarked as a best value within this paper	7.34 x 10-1 S cm-1	—	—	SI Table Exact Reported	SI p.S10 · Electronic/electrochemical characterizations · Table S4

1D rod-like Cu-HHTP powder · Powder

Pressed pellet prepared with approximately 5 mg material in a 5 mm diameter die under 1.5 tons pressure.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
1D Cu-HHTP powder electrical conductivity	3.00 x 10-2 S cm-1	—	—	SI Table Exact Reported	SI p.S10 · Electronic/electrochemical characterizations · Table S4

2D sheet-like Cu-HHTP powder · Powder

Pressed pellet prepared with approximately 5 mg material in a 5 mm diameter die under 1.5 tons pressure.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
2D Cu-HHTP powder electrical conductivity	2.70 x 10-2 S cm-1	—	—	SI Table Exact Reported	SI p.S10 · Electronic/electrochemical characterizations · Table S4