Diffraction Structure — Electrochemical Synthesis of Large Area Two-Dimensional Metal–Organic Framework Films on Copper Anodes

Measurement evidence

Diffraction Structure

Electrochemical Synthesis of Large Area Two-Dimensional Metal–Organic Framework Films on Copper Anodes · Liu Y., Wei Y., Liu M. et al. · Angewandte Chemie - International Edition · 2021 · 2887-2891

1 measurement group · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

GIWAXS

X-ray diffraction and scattering

As-grown Cu3(HHTP)2 MOF film on single-crystal Cu(100) anode · Thin Film

Experimental GIWAXS compared with theoretical pattern for A-A stacked Cu3(HHTP)2.

Context
Pristine Cu3(HHTP)2 MOF film
Measurement source
main p.2 · Structure · Figure 2b
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
GIWAXS (002) peak2theta about 27.5 deg assigned to (002)——Text
Approximate		main p.2 · Structure · Figure 2b
GIWAXS (100) peak2theta about 4.7 deg assigned to (100)——Text
Approximate		main p.2 · Structure · Figure 2b
GIWAXS (200) peak2theta about 9.5 deg assigned to (200)——Text
Approximate		main p.2 · Structure · Figure 2b
GIWAXS (210) peak2theta about 12.5 deg assigned to (210)——Text
Approximate		main p.2 · Structure · Figure 2b