Measurement evidence
Macrocyclic ligand-driven ion selectivity and high surface area in a 2D conductive MOF · Pham H.T.B., Choi J.Y., Fang X. et al. · Chem · 2024 · 199-210
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Cu-EP/Super P/PTFE modified glassy carbon electrode · Electrode
100-500 mV/s in 0.40-0.45 V versus Ag/Ag+ non-faradaic window in 1 M Na2CO3
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| double-layer capacitance | 0.65 mF/cm2 | — | — | Figure Axis Rounded Reported | 204 · Electrochemical properties · Figure 4D |
Cu-EP/Super P/PTFE modified glassy carbon electrode · Electrode
1 M Na2CO3; 0 V versus Ag/Ag+; 10 mV AC; 1 MHz to 50 mHz
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Warburg coefficientMarked as a best value within this paper | 1100 | — | — | Text Rounded Reported | 205 · Electrochemical properties · Figure 4F |
Cu-EP/Super P/PTFE modified glassy carbon electrode · Electrode
1 M aqueous Na2CO3; modified GCE; Ag/Ag+ reference; Pt counter; scan rate 10 mV/s for main CV
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electrochemical capacitance in 1 M Na2CO3Marked as a best value within this paper | 130 F/g | — | — | SI Table Exact Reported | S26 · Electrochemical characterization · Table S5 |
| extra reduction peak | -0.3 V versus Ag/Ag+ | — | — | Text Approximate | 205 · Electrochemical properties · Figure 4A |
Cu-HHTC/Super P/PTFE modified glassy carbon electrode · Electrode
100-500 mV/s in 0.40-0.45 V versus Ag/Ag+ non-faradaic window in 1 M Na2CO3
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| double-layer capacitance | 0.22 mF/cm2 | — | — | Figure Axis Rounded Reported | 204 · Electrochemical properties · Figure 4D |
Cu-HHTC/Super P/PTFE modified glassy carbon electrode · Electrode
1 M Na2CO3; 0 V versus Ag/Ag+; 10 mV AC; 1 MHz to 50 mHz
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Warburg coefficient | 45000 | — | — | Text Rounded Reported | 205 · Electrochemical properties · Figure 4F |
Cu-HHTC/Super P/PTFE modified glassy carbon electrode · Electrode
1 M aqueous Na2CO3; modified GCE; Ag/Ag+ reference; Pt counter; scan rate 10 mV/s for main CV
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| electrochemical capacitance in 1 M Na2CO3 | 3.68 F/g | — | — | SI Table Exact Reported | S26 · Electrochemical characterization · Table S5 |