Sensing Application — In-Plane Oriented Two-Dimensional Conjugated Metal-Organic Framework Films for High-Performance Humidity Sensing

3 measurement groups · 10 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

bulk powder form HIB-Cu sensor device · Powder

N2 and H2O/N2 pulses with same period and duty cycle of 300 s.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
powder test pulse period and duty cycle	300 s period and 300 s duty cycle	—	—	Caption Exact Reported	23 · Supporting Figure S16 · Figure S16
HIB-Cu powder humidity recovery time	200 s	—	—	SI Table Exact Reported	21 · Supporting Table S1 · Table S1
HIB-Cu powder humidity response time	180 s	—	—	SI Table Exact Reported	21 · Supporting Table S1 · Table S1

HIB-Cu film chemiresistive humidity sensor · Electrode

Cyclohexane and ethanol streams tested instead of H2O; nitrogen baseline at 1 V for 40 min.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
cyclohexane response	no current/conductivity change observed	—	—	Text Qualitative	1151 · Results · Figure S17
ethanol response	sensing behaviour resembled humidity sensor	—	—	Text Qualitative	1151 · Results · Figure S17

HIB-Cu film chemiresistive humidity sensor · Electrode

Nitrogen stream with H2O/N2 pulses; constant 1 V; 60 s period/duty in main figure and 120 s step/purge protocol in SI methods.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
reproducibility cycles	more than 9 cycles	—	—	Text Approximate	1150 · Results · Figure 5c
HIB-Cu film H2O detection range	200-1000 ppm	—	—	SI Table Range	21 · Supporting Table S1 · Table S1
HIB-Cu film humidity recovery timeMarked as a best value within this paper	40 s, 10% decay time	—	—	Text Rounded Reported	1150 · Results · Figure 5d; Table S1
HIB-Cu film humidity detection range in RH	~0.9%	0.009 relative humidity fraction	—	SI Table Approximate	22 · Supporting Table S2 · Table S2
HIB-Cu film humidity response timeMarked as a best value within this paper	~21 s, 90% saturation rise time	—	—	Text Approximate	1150 · Results · Figure 5d; Table S1