Porosity — Photoinduced Charge-Carrier Generation in Epitaxial MOF Thin Films: High Efficiency as a Result of an Indirect Electronic Band Gap?

2 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Free-base porphyrin Zn-SURMOF 2 on glass-coated QCM sensor · Thin Film

Q-Sense E4 with flow module; 25 +/- 0.02 deg C; 100 uL/min; exposure to acetonitrile and I-/I3- in acetonitrile.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Frequency shift after acetonitrile injection	Delta f = ~80 Hz	—	—	Caption Approximate	29 / p030 · Supplementary Figures · Figure S19
Dissipation factor after solvent/electrolyte injection	Delta D = 1 x 10^-6	—	—	Caption Rounded Reported	29 / p030 · Supplementary Figures · Figure S19
Frequency shift after I-/I3- electrolyte injection	Delta f = ~40 Hz	—	—	Caption Approximate	29 / p030 · Supplementary Figures · Figure S19

Pd porphyrin Zn-SURMOF 2 on glass-coated QCM sensor · Thin Film

Q-Sense E4 with flow module; 25 +/- 0.02 deg C; 100 uL/min; exposure to acetonitrile and I-/I3- in acetonitrile.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Frequency shift after acetonitrile injection	Delta f = ~550 Hz	—	—	Caption Approximate	31 / p032 · Supplementary Figures · Figure S21
Dissipation factor after solvent/electrolyte injection	Delta D = 1.5 x 10^-6	—	—	Caption Rounded Reported	31 / p032 · Supplementary Figures · Figure S21
Frequency shift after I-/I3- electrolyte injection	Delta f = ~60 Hz	—	—	Caption Approximate	31 / p032 · Supplementary Figures · Figure S21