Other — Mixed metal conductive MOFs constructed from Trypan blue linked metal nodes: characteristic features and electrochemical performance

4 measurement groups · 19 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cu-Co-Try MOF powder (P1) · Powder

Thermogravimetric analysis of powder sample

Measurement source: 3895-3897 · Thermogravimetric analysis · Fig. 7; Table 2

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
P1 TGA weight loss at 194.14 C	15.2	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P1 TGA weight loss at 271.9 C	18.29	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P1 TGA weight loss at 346.93 C	13.56	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P1 TGA weight loss at 447.27 C	13.473	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P1 stability below 130 C	no weight loss below 130 C	—	—	Text Exact Reported	3895 · Thermogravimetric analysis · Fig. 7

Cu-Zn-Try MOF powder (P2) · Powder

Thermogravimetric analysis of powder sample

Measurement source: 3895-3897 · Thermogravimetric analysis · Fig. 7; Table 2

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
P2 TGA weight loss at 135.53 C	11.414	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P2 TGA weight loss at 277.46 C	10.496	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P2 TGA weight loss at 367.43 C	22.316	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P2 TGA weight loss at 501.69 C	10.706	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P2 stability below 130 C	no weight loss below 130 C	—	—	Text Exact Reported	3895 · Thermogravimetric analysis · Fig. 7

Cu-Er-Try MOF powder (P3) · Powder

Thermogravimetric analysis of powder sample

Measurement source: 3895-3897 · Thermogravimetric analysis · Fig. 7; Table 2

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
P3 TGA weight loss at 173.5 C	4.66	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P3 TGA weight loss at 325.64 C	15.838	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P3 TGA weight loss at 420.9 C	15.972	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P3 TGA weight loss at 567.69 C	23.169	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P3 stability below 130 C	no weight loss below 130 C	—	—	Text Exact Reported	3895 · Thermogravimetric analysis · Fig. 7

Cu-Yb-Try MOF powder (P4) · Powder

Thermogravimetric analysis of powder sample

Measurement source: 3895-3897 · Thermogravimetric analysis · Fig. 7; Table 2

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
P4 TGA weight loss at 139.69 C	5.249	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P4 TGA weight loss at 253.06 C	14.295	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P4 TGA weight loss at 442.23 C	46.821	—	—	Table Exact Reported	3897 · Table 2 · Table 2
P4 stability below 130 C	no weight loss below 130 C	—	—	Text Exact Reported	3895 · Thermogravimetric analysis · Fig. 7