Microscopy Morphology — Large-Area Metal–Organic Framework Glasses for Efficient X-Ray Detection

Measurement evidence

Microscopy Morphology

Large-Area Metal–Organic Framework Glasses for Efficient X-Ray Detection · Zhu X., He T., Song X. et al. · Advanced Materials · 2024 · 2412432

1 measurement group · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

SEM and EDS elemental mapping

Scanning electron microscopyElemental microanalysis and mapping

ZnPIm MOF glass film · Thin Film

Zeiss Merlin SEM; EDX/EDS elemental mapping for Zn, P, N and O.

Context
Pristine ZnPIm glass film compared with powder and pressed disc.
Measurement source
main p.2 · 2.1. Synthesis, Structure and Characterization · Figure 2c-d; Figures S7-S9
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Pressed-disc morphologyPressed ZnPIm disc shows a discontinuous surface with clearly visible particles.——Text
Qualitative		main p.2 · 2.1. Synthesis, Structure and Characterization · Figure 2c
Elemental distributionUniform distribution of Zn, P, N, and O within the MOF glass and MOF disc.——Text
Qualitative		main p.2 · 2.1. Synthesis, Structure and Characterization · Figure 2d; Figure S9
Demonstrated glass-film dimensionsGlass films photographed at 1 x 1 cm, 2 x 2 cm, 3 x 3 cm and 4 x 4 cm.——Figure Axis
Exact Reported		SI p.S11 · Supplementary Figures · Figure S8
Glass-film surface morphologyExtremely smooth surface, devoid of grain boundaries or distinguishable domains.——Text
Qualitative		main p.2 · 2.1. Synthesis, Structure and Characterization · Figure 2c