Other — Large-Area Metal–Organic Framework Glasses for Efficient X-Ray Detection

4 measurement groups · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

ZnBTA MOF glass detector · Electrode

Supplementary thermal analysis for ZnBTA; TGA from 25 to 500 C under N2 and DSC beginning from 30 C under N2 flow.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ZnBTA melting temperature from DSC label	Tm = 98 C	—	—	Figure Axis Rounded Reported	SI p.S9 · Supplementary Figures · Figure S5d

ZnHBIm MOF glass detector · Electrode

Supplementary thermal analysis for ZnHBIm; TGA from 25 to 500 C under N2 and DSC beginning from 30 C under N2 flow.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ZnHBIm melting temperature from DSC label	Tm = 164 C	—	—	Figure Axis Rounded Reported	SI p.S9 · Supplementary Figures · Figure S5b

Dry ZnPIm powder · Powder

TGA under N2 at 5 C/min; DSC with heating/cooling rate 10 C/min under N2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Melting temperature Tm	158 C	—	—	Text Exact Reported	main p.2 · 2.1. Synthesis, Structure and Characterization · Figure S5
TGA thermal stability threshold	No significant weight loss below 200 C	—	—	Text Rounded Reported	main p.2 · 2.1. Synthesis, Structure and Characterization · Figure S4

ZnTzH MOF glass detector · Electrode

Supplementary thermal analysis for ZnTzH; TGA from 25 to 500 C under N2 and DSC beginning from 30 C under N2 flow.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ZnTzH melting temperature from DSC label	Tm = 198 C	—	—	Figure Axis Rounded Reported	SI p.S9 · Supplementary Figures · Figure S5c