Two-probe electrical conductivity from ohmic I-V curves and impedance responses
Ga9HHTP4 multi-sample comparison series · Powder
Self-supported MOF pellets in custom-built Swagelok cells under ambient conditions; measurements under pressure capped at 2 MPa.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Electrical conductivity of ACN-soaked Ga9HHTP4 | ~1.8e-4 S cm-1 from Fig. 4a/S21 | 0.00018 S cm-1 | visual estimate from log axis | Figure Axis Approximate | p005 · Charge transport properties · Fig. 4a |
| Electrical conductivity of DMF-soaked Ga9HHTP4 | ~1.5e-5 S cm-1 from Fig. 4a/S21 | 0.000015 S cm-1 | visual estimate from log axis | Figure Axis Approximate | p027 · Figure S21 · Fig. S21 |
| Electrical conductivity of ethanol-soaked Ga9HHTP4 | ~2.0e-5 S cm-1 from Fig. 4a/S21 | 0.00002 S cm-1 | visual estimate from log axis | Figure Axis Approximate | p027 · Figure S21 · Fig. S21 |
| Average electrical conductivity of heat-treated Ga9HHTP4 | 0.15 mS cm-1 | 0.00015 S cm-1 | — | Text Exact Reported | p005 · Charge transport properties · Fig. 4a |
| Average electrical conductivity of pristine Ga9HHTP4Marked as a best value within this paper | 0.49 mS cm-1 | 0.00049 S cm-1 | — | Text Exact Reported | p005 · Charge transport properties · Fig. 4a |
| Electrical conductivity of water-soaked Ga9HHTP4 | ~1.5e-5 S cm-1 from Fig. 4a | 0.000015 S cm-1 | visual estimate from log axis | Figure Axis Approximate | p005 · Charge transport properties · Fig. 4a |