Other — Continuous and reversible tuning of inter-layer spacings in two-dimensional conductive metal organic frameworks

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Ga9HHTP4 multi-sample comparison series · Powder

Weight loss of pristine, heat-treated and ambient-exposed Ga9HHTP4 from 30 to 200 deg C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HT-Ga9HHTP4 weight loss from 30-200 deg C	~7% loss in weight between 30-200 deg C	—	~	Text Approximate	p004 · Solvent removal/exchange in Ga9HHTP4 · Fig. S9
Pristine Ga9HHTP4 weight loss from 30-200 deg C	~17% loss in weight between 30-200 deg C	—	~	Text Approximate	p004 · Solvent removal/exchange in Ga9HHTP4 · Fig. S9

Ni6HHTT3 multi-sample comparison series · Powder

Weight loss of pristine and heat-treated Ni6HHTT3 from 30 to 200 deg C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HT-Ni6HHTT3 weight loss from 30-200 deg C	~10% loss in weight between 30-200 deg C	—	~	Text Approximate	p005 · Solvent removal in Ni6HHTT3 · Fig. S15
Pristine Ni6HHTT3 weight loss from 30-200 deg C	~35% loss in weight between 30-200 deg C	—	~	Text Approximate	p005 · Solvent removal in Ni6HHTT3 · Fig. S15