Measurement evidence
NH2-UiO-66 Metal-Organic Framework Nanoparticles for Hydroxide Ion Conductive Photoswitches · Wang S., Fan S., Fang Z. et al. · ACS Applied Nano Materials · 2021 · 8352-8359
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
NH2-UiO-66-10-OH · Pellet
XRD patterns of NH2-UiO-66-10 and NH2-UiO-66-50 before and after KOH/conductivity testing.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| framework crystallinity after KOH/conductivity test | NH2-UiO-66-10-OH after test and NH2-UiO-66-50-OH after test retain XRD features; -50 remains more crystalline | — | — | Qualitative Qualitative | p004 · Additional figures · Figure S3 |
NH2-UiO-66-0 · Powder
XRD patterns of NH2-UiO-66 samples prepared with 0, 10, 50, and 100 equiv acetic-acid modulator.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| XRD crystallinity trend with acetic-acid modulator | crystallinity increases from NH2-UiO-66-0/10 to NH2-UiO-66-50/100 | — | — | Qualitative Qualitative | p002 · Additional figures · Figure S1b |
NH2-UiO-66-50 · Powder
XRD patterns compared against simulated NH2-UiO-66.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| reported nanopore size | 1 nm | 1 nm | — | Text Rounded Reported | p002 · Introduction |
| reported triangular window size | 0.6 nm | 0.6 nm | — | Text Rounded Reported | p002 · Introduction |
| XRD characteristic peak | 7.36 deg 2theta | 7.36 deg 2theta | — | Text Exact Reported | p002 · Result and Discussion · Figure 1c |
| XRD characteristic peak | 8.48 deg 2theta | 8.48 deg 2theta | — | Text Exact Reported | p002 · Result and Discussion · Figure 1c |