Porosity — NH2-UiO-66 Metal-Organic Framework Nanoparticles for Hydroxide Ion Conductive Photoswitches

Measurement evidence

Porosity

NH2-UiO-66 Metal-Organic Framework Nanoparticles for Hydroxide Ion Conductive Photoswitches · Wang S., Fan S., Fang Z. et al. · ACS Applied Nano Materials · 2021 · 8352-8359

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

CO2 adsorption isotherm (Micromeritics ASAP 2020)

Gas sorption and porosity

NH2-UiO-66-10-OH · Pellet

CO2 adsorption isotherms of NH2-UiO-66-10 and NH2-UiO-66-10-OH at 298 K.

Temperature: 298
Atmosphere: CO2
Context: KOH-treated OH-loaded sample compared with pristine NH2-UiO-66-10
Measurement source: p003 · Results · Figure 2c

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CO2 adsorption of NH2-UiO-66-10 at P/P0 about 0.015	~12 cc g^-1 at P/P0 ~0.015	12 cm3 g^-1	—	Visual Estimate Approximate	p003 · Results · Figure 2c
CO2 adsorption of NH2-UiO-66-10-OH at P/P0 about 0.015	~36 cc g^-1 at P/P0 ~0.015	36 cm3 g^-1	—	Visual Estimate Approximate	p003 · Results · Figure 2c