Porosity — Catalytic Metal-Organic Framework-Functionalized Inverse-Opal Architectured Polymeric Separator for High-Performance Li-S Batteries

3 measurement groups · 15 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

ZIF-PIO-3 separator · Thin Film

Solid-liquid contact angle with battery electrolyte on separators.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Electrolyte contact angle	about 40 deg	—	—	Text Approximate	5 · Results and Discussion · Figure S8
Electrolyte contact angle	22.7 deg	—	—	Text Exact Reported	5 · Results and Discussion · Figure S8
Electrolyte contact angle	22.5 deg	—	—	Text Exact Reported	5 · Results and Discussion · Figure S8
Electrolyte contact angleMarked as a best value within this paper	12.8 deg	—	—	Text Exact Reported	5 · Results and Discussion · Figure S8
Electrolyte contact angle	13.1 deg	—	—	Text Exact Reported	5 · Results and Discussion · Figure S8

ZIF-PIO-3 separator · Thin Film

Separators immersed in liquid electrolyte for 12 h; uptake calculated from before/after mass.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Electrolyte uptake	156.1%	—	—	Text Exact Reported	5 · Results and Discussion · Figure 3b
Electrolyte uptake	262.1%	—	—	Text Exact Reported	5 · Results and Discussion · Figure 3b
Electrolyte uptakeMarked as a best value within this paper	275.6%	—	—	Text Exact Reported	5 · Results and Discussion · Figure 3b
Electrolyte uptake	238.8%	—	—	Text Exact Reported	5 · Results and Discussion · Figure 3b
Electrolyte uptake	250.5%	—	—	Text Exact Reported	5 · Results and Discussion · Figure 3b

ZIF-PIO-3 separator · Thin Film

Separator porosity comparison for PE, PIO-3, PIO-5, ZIF-PIO-3 and ZIF-PIO-5.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Separator porosity	42.4%	—	—	Text Exact Reported	5 · Results and Discussion · Figure 3a
Separator porosity	about 70%	—	—	Figure Axis Approximate	5 · Results and Discussion · Figure 3a
Separator porosityMarked as a best value within this paper	about 73%	—	—	Figure Axis Approximate	5 · Results and Discussion · Figure 3a
Separator porosity	about 64%	—	—	Figure Axis Approximate	5 · Results and Discussion · Figure 3a
Separator porosity	about 69%	—	—	Figure Axis Approximate	5 · Results and Discussion · Figure 3a