Microscopy Morphology — Ligand-Insertion Strategy for Constructing 2D Conjugated Metal–Organic Framework with Large Pore Size for Electrochemical Analytics

Measurement evidence

Microscopy Morphology

Ligand-Insertion Strategy for Constructing 2D Conjugated Metal–Organic Framework with Large Pore Size for Electrochemical Analytics · Wang X.-Z., Chen Y., Cao X.-M. et al. · Angewandte Chemie - International Edition · 2025 · e202413115

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

SEM, HRTEM and SAED

Scanning electron microscopyTransmission electron microscopy

As-prepared Cu3(HHTP)(DHBQ)1.5/1.53 black powder · Powder

SEM on JEOL JSM-7500F at 5 kV; HRTEM/SAED on JEOL JEM-2100F at 200 kV after ethanol dispersion was dried on microgrid copper mesh.

Geometry
powder/nanoparticles on TEM grid
Context
pristine_framework
Measurement source
3-4 · Structural Characterization on the Sample · Figure 1d-e; Figure S10
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
HRTEM adjacent-pore distance3.5 nm——Text
Exact Reported		4 · Structural Characterization on the Sample · Figure 1e
HRTEM lattice-stripe spacing1.77 nm——Text
Exact Reported		4 · Structural Characterization on the Sample · Figure S10