Measurement evidence
Cooperative Proton and Li-ion Conduction in a 2D-Layered MOF via Mechanical Insertion of Lithium Halides · Sarango-Ramirez M.K., Donoshita M., Yoshida Y. et al. · Angewandte Chemie - International Edition · 2023 · e202301284
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Ti-dobdc pristine · Pellet
TGA with N2 flow and 5 deg C min^-1 ramp.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| framework stable up to temperature | 523 K | — | — | Text Rounded Reported | 2 · Results · Figure S3 |
Ti-dobdc-LiBr (MOF:LiBr = 1:1) · Pellet
TGA with N2 flow and 5 deg C min^-1 ramp.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| thermal stability after LiX intercalation | 623 K | — | — | Text Rounded Reported | 2 · Results · Figure S3 |
Ti-dobdc-LiCl (MOF:LiCl = 1:1) · Pellet
TGA with N2 flow and 5 deg C min^-1 ramp.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| thermal stability after LiX intercalation | 623 K | — | — | Text Rounded Reported | 2 · Results · Figure S3 |
Ti-dobdc-LiI (MOF:LiI = 1:1) · Pellet
TGA with N2 flow and 5 deg C min^-1 ramp.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| thermal stability after LiX intercalation | 623 K | — | — | Text Rounded Reported | 2 · Results · Figure S3 |