Measurement evidence
From non-conductive MOF to proton-conducting metal-HOFs: a new class of reversible transformations induced by solvent-free mechanochemistry · Lupa-Myszkowska M., Oszajca M., Matoga D. · Chemical Science · 2023 · 14176-14181
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Mn-HOF-FA powder · Powder
CO2 adsorption measurement at 195 K for Mn-HOF-MA and Mn-HOF-FA
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Mn-HOF-FA CO2 uptake near p/p0 0.9 | approximately 6.5 cm3 STP g-1 | — | — | Visual Estimate Approximate | p024 · Figures and Tables · Figure S38 |
| Mn-HOF-MA CO2 uptake near p/p0 0.9 | approximately 6.5 cm3 STP g-1 | — | — | Visual Estimate Approximate | p024 · Figures and Tables · Figure S38 |
Mn-HOF-FA powder · Powder
N2 adsorption measurement at 77 K for Mn-HOF-MA and Mn-HOF-FA
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Mn-HOF-FA N2 uptake near p/p0 1.0 | approximately 15-16 cm3 STP g-1 | — | — | Visual Estimate Approximate | p024 · Figures and Tables · Figure S37 |
| Mn-HOF-MA N2 uptake near p/p0 1.0 | approximately 21 cm3 STP g-1 | — | — | Visual Estimate Approximate | p024 · Figures and Tables · Figure S37 |
Mn-HOF-FA powder · Powder
H2O adsorption at 293 K for JUK-1, JUK-2, Mn-HOF-FA and Mn-HOF-MA
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Mn-HOF-FA H2O uptake near p/p0 0.9 | approximately 320-340 cm3 STP g-1 | — | — | Visual Estimate Approximate | p026 · Figures and Tables · Figure S40 |
| JUK-2 H2O uptake near p/p0 0.9 | approximately 1200 cm3 STP g-1 | — | — | Visual Estimate Approximate | p026 · Figures and Tables · Figure S40 |
| Mn-HOF-MA H2O uptake near p/p0 0.9 | approximately 850-900 cm3 STP g-1 | — | — | Visual Estimate Approximate | p026 · Figures and Tables · Figure S40 |