XRD, FTIR, TGA
Ni3(HITP)2 powder · Powder
Crystal/chemical/thermal characterisation of Ni3(HITP)2 powder.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| FTIR aromatic C-C stretching peak | 1428 cm^-1 | — | — | Text Exact Reported | p006 · 3 · Figure 3B |
| FTIR aromatic C-C stretching peak | 1516 cm^-1 | — | — | Text Exact Reported | p006 · 3 · Figure 3B |
| FTIR C=C stretching peak | 1620 cm^-1 | — | — | Text Exact Reported | p006 · 3 · Figure 3B |
| FTIR C-N stretching peak | 1326 cm^-1 | — | — | Text Exact Reported | p006 · 3 · Figure 3B |
| FTIR N-H oscillation peak | 860 cm^-1 | — | — | Text Exact Reported | p006 · 3 · Figure 3B |
| FTIR water or -NH peak | 3429 cm^-1 | — | — | Text Exact Reported | p006 · 3 · Figure 3B |
| Ni3(HITP)2 powder XRD (001) peak | 2theta = 27.3 deg | — | — | Text Exact Reported | p006 · 3 · Figure 3A |
| Ni3(HITP)2 powder XRD (100) peak | 2theta = 4.7 deg | — | — | Text Exact Reported | p006 · 3 · Figure 3A |
| Ni3(HITP)2 powder XRD additional reported peak | 2theta = 12.6 deg | — | — | Text Exact Reported | p006 · 3 · Figure 3A |
| Ni3(HITP)2 powder XRD (200) peak | 2theta = 9.5 deg | — | — | Text Exact Reported | p006 · 3 · Figure 3A |
| TGA structural collapse onset | above 300 deg C | — | above | Text Approximate | p006 · 3 · Figure 3C |
| TGA hydrate-water mass-loss stage | 0-200 deg C | — | — | Text Range | p006 · 3 · Figure 3C |
| TGA physical-adsorption mass-loss stage | 200-300 deg C | — | — | Text Range | p006 · 3 · Figure 3C |