Microscopy Morphology — Interconnected Lamellar 3D Semiconductive PCP for Rechargeable Aqueous Zinc Battery Cathodes

2 measurement groups · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

As-prepared VO-HHTP black powder · Powder

HRTEM images viewed along [010] and [001].

Context: pristine framework powder
Measurement source: p.3 / article p.2411386-3 · Results and Discussion · Figure 2c,d

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HRTEM lattice spacing for (100)	approximately 1.86 nm	—	—	Text Approximate	p.3 / article p.2411386-3 · Results and Discussion · Figure 2c
Honeycomb porous structure observation	regular honeycomb-like porous structure	—	—	Qualitative Qualitative	p.3 / article p.2411386-3 · Results and Discussion · Figure 2d

As-prepared VO-HHTP black powder · Powder

As-prepared powder morphology.

Context: pristine framework powder
Measurement source: p.2 / article p.2411386-2 · Results and Discussion · Figure 2a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Rod diameter upper bound	20 nm	—	—	Text Rounded Reported	p.2 / article p.2411386-2 · Results and Discussion · Figure 2a
Rod diameter lower bound	10 nm	—	—	Text Rounded Reported	p.2 / article p.2411386-2 · Results and Discussion · Figure 2a
Rod length	approximately 500 nm	—	—	Text Approximate	p.2 / article p.2411386-2 · Results and Discussion · Figure 2a