Porosity — Interconnected Lamellar 3D Semiconductive PCP for Rechargeable Aqueous Zinc Battery Cathodes

Measurement evidence

Porosity

Interconnected Lamellar 3D Semiconductive PCP for Rechargeable Aqueous Zinc Battery Cathodes · Lin Z., Otake K.-I., Kajiwara T. et al. · Small · 2025 · 2411386

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 gas sorption/BET surface area

Gas sorption and porosity

As-prepared VO-HHTP black powder · Powder

N2 probe gas at 77 K using BEL-mini X surface area analyzer.

Temperature: 77
Atmosphere: N2
Geometry: powder adsorption isotherm
Context: pristine framework powder
Measurement source: p.4 / article p.2411386-4 · Results and Discussion · Figure S6

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET specific surface areaMarked as a best value within this paper	590.41 m2 g-1	—	—	Figure Axis Rounded Reported	SI p.5 / rendered p006 · Supporting figures · Figure S6