Powder X-ray diffraction (PXRD)
Cu3(HITP)2 powder scraped from copper foil for PXRD · Powder
Rigaku Miniflex, Cu Kalpha 1.54 A; 2 to 50 deg at 5 deg min-1, 0.02 deg step.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| (001) peak position and sharpness | (001) at 2theta = 27.5 deg; significantly sharper than typically reported | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| CuO side-product PXRD peak | 2theta = 35.6 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| CuO side-product PXRD peak | 2theta = 38.6 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| hexagonal lattice parameter a | a = b = 21.7 A | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| hexagonal lattice parameter b | a = b = 21.7 A | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| hexagonal lattice parameter c | c = 3.2 A | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| Cu3(HITP)2 PXRD MOF reflection at 2theta 12.6 | 2theta = 12.6 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| Cu3(HITP)2 PXRD MOF reflection at 2theta 16.6 | 2theta = 16.6 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| Cu3(HITP)2 PXRD MOF reflection at 2theta 27.4 | 2theta = 27.4 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| Cu3(HITP)2 PXRD MOF reflection at 2theta 4.7 | 2theta = 4.7 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| Cu3(HITP)2 PXRD MOF reflection at 2theta 9.6 | 2theta = 9.6 deg | — | — | Text Exact Reported | p006 · Results and discussion · Figure 3d |
| unassigned PXRD peak | around 24 deg | — | — | Text Approximate | p006 · Results and discussion · Figure 3d |