Scanning electron microscopy (SEM)
Electrochemically synthesised Cu3(HHTP)2 on Pt/glass IDE (2 h growth) · Electrode
Zeiss Merlin, InLens detector, 3 kV, 100 pA, 7 mm WD; separate samples at 0 min, 10 min, 2 h; ImageJ particle sizing
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Particle diameter, as-deposited Cu nanoparticles (0 min) | 15-20 nm | — | range 15-20 nm | Text Range | 5 · 3.2 Morphology and Resistance Studies · Figure 4b |
| Particle dimensions after 10 min growth | 40-65 nm | — | range 40-65 nm | Text Range | 5 · 3.2 Morphology and Resistance Studies · Figure 4d |
| Particle dimensions after 2 h growth | 60-160 nm | — | range 60-160 nm | Text Range | 5 · 3.2 Morphology and Resistance Studies · Figure 4f |